admin

Home/admin

About admin

This author has not yet filled in any details.
So far admin has created 6 blog entries.

best-moulding-manufacturer-in-china

Top Injection moulding manufacturer More than a supplier Corelmould is a professional and dedicated plastic injection moulding manufacturer in shenzhen , South China.Our #1 priority is you, our customer. We believe in our moulds and hold ourselves to the highest standards. We truly care about your end products and sales as much as you do, which is [...]

By | 2017-03-18T09:05:52+00:00 October 23rd, 2014|Uncategorized|Comments Off on best-moulding-manufacturer-in-china

Even wall thickness

Thick sections and non-uniform walls cause problems Keep wall thickness as uniform as possible. Use gradual transitions between thick and thin sections.  Wall thickness must suit both function and process.  Wall thickness guide range is 0.75 mm to 3 mm for reinforced materials 0.5 mm to 5 mm for unreinforced materials /li_item] Un-even wall thickness tend to have bad injection result, both accuracy and strength. Parts that might be made as solid shapes in traditional materials must be formed quite differently in plastics. Moulded plastics do not lend themselves to solid forms. There are two principal reasons for this. First, plastics are processed with heat but are poor conductors of heat. This means that thick sections take a very long time to cool and so are costly to make. The problems posed by shrinkage are equally severe. During cooling, plastics undergo a volume reduction. In thick sections, this either causes the surface of the part to cave in to form an unsightly sink mark or produces an internal void. Furthermore, plastics materials are expensive; it is only high-speed production methods and net-shape forming that make mouldings viable. Thick sections waste material and are simply uneconomic. So solid shapes that would do the job well in wood or metal must be transformed to a 'shell' form in plastics. This is done by hollowing out or 'coring' thick parts so you are left with a component which regardless of complexity is composed essentially of relatively thin walls joined by curves, angles, corners, ribs, steps and offsets. As far as possible, all these walls should be the same thickness. It is not easy to generalise what the wall thickness should be. The wall plays a part both in design concept and embodiment. The wall must be thick enough to do its job; it must be strong enough or stiff enough or cheap enough. But it must also be thin enough to cool quickly and thick enough to allow efficient mould filling. If the material is inherently strong or stiff the wall can be thinner. As a general guide, wall thicknesses for reinforced materials should be 0.75 mm to 3 mm, and those for unfilled materials should be 0.5 mm to 5 mm. Ideally, the entire component should be a uniform thickness - the nominal wall thickness. In practice that is often not possible; there must be some variation in thickness to accommodate functions or aesthetics. It is very important to keep this variation to a minimum. A plastics part with thickness variations will experience differing rates of cooling and shrinkage. The result is likely to be a part that is warped and distorted, one in which close tolerances become impossible to hold. Where variations in thickness are unavoidable, the transformation between the two should be gradual not sudden so instead of a step, use a ramp or a curve to move from thick to thin. [...]

By | 2017-03-18T09:05:52+00:00 September 17th, 2014|Design guides|Comments Off on Even wall thickness